Pengaruh Pemanfaatan Plastik Polyethylene Terephalate Pada Campuran Laston Lapis Pengikat

  • Ifani Mita'ul Habibah Politeknik Negeri Banyuwangi
  • Mirza Ghulam Rifqi Politeknik Negeri Banyuwangi
  • Dadang Dwi Pranowo Politeknik Negeri Banyuwangi
Keywords: AC-BC, PET, Dry process, Marshall parameters, General specification of Bina Marga 2018

Abstract

Plastic Polyethylene Terephthalate (PET) waste can be utilized as an added ingredient in a mixture of fastening concrete asphalt (Laston AC-BC). The purpose of this research is to know the influence of the utilization of PET plastics (Polyethylene Terephthalate) on the layer of concrete asphalt binder (Laston AC-BC) using the Marshall method by referring to the design guidelines and implementation of the heat-paved mixture using plastic waste 2019 and the general specification of Highways 2018. 

This research is done with the addition of PET worms on the asphalt mixture using a dry process. PET levels added in the asphalt mixture are 4%, 4.5%, and 5% of the weight of the asphalt. 

After the Marshall testing, the results of PET additions to the Laston AC-BC mixture can improve stability. The highest stability value is the addition of PET 5%. The stability value due to PET addition is greater than without the addition of PET. The best PET replenishment rate for asphalt mixture is 5% because, in addition to high stability value, other Marshall parameters such as Flow, VIM, VMA, VFB, and MQ also qualify for the design guidelines and implementation of the hot paved mixture using plastic waste 2019. Value of Optimum asphalt content (KAO) obtained at a 6% asphalt rate with the addition of PET 5%.

References

Pedoman Bahan Konstruksi Bangunan dan Rekayasa Sipil. 2019. Perancangan dan Pelaksanaan Campuran Beraspal Panas Menggunakan Limbah Plastik. Jakarta: JDIH Kementerian PUPR.

Prameswari, P. A., Pratomo, P., & Harianto, D. 2016. Pengaruh Pemanfaatan PET pada Laston Lapis Pengikat Terhadap Parameter Marshall. JRSSD, 294-305.

SNI 03-4426-1997. 1997. Metode Pengujian Ketahanan Agregat dengan Alat Tumbuk. Jakarta: Pusran Balitbang PU.

SNI 03-6723-2002. 2002. Spesifikasi Bahan Pengisi Untuk Campuran Beraspal. Jakarta: Badan Standardisasi Nasional.

SNI 06-2441-2011. 2011. Pengujian Berat Jenis Aspal Padat. Jakarta: Badab Standardisasi Nasional.

SNI 1969:2016. 2016. Cara Uji Berat Jenis dan Penyerapan Air Agregat Kasar. Jakarta: Badan Standarisasi Nasional.

SNI 1970:2016. 2016. Cara Uji Berat Jenis dan Penyerapan Air Agregat Halus. Jakarta: Badan Standarisasi Nasional.

SNI 2417:2008. 2008. Cara Uji Keausan Agregat Dengan Mesin Abrasi Los Angeles. Jakarta: Badan Standarisasi Nasional.

SNI 2432:2011. 2011. Cara Uji Daktilitas Aspal. Jakarta: Bdan Standarisasi Nasional.

SNI 2433:2011. 2011. Cara Uji Titik Nyala dan Ttitik Bakar Aspal Dengan Alat Cleveland Open Cup. Jakarta: Badan Standarisasi Nasional.

SNI 2434:2011. 2011. Cara Uji Titik Lembek Aspal Dengan Alat Cincin dan Bola (ring and ball). Jakarta: Badan Standarisasi Nasional.

SNI ASTM C117:2012. 2012. Metode Uji Bahan Yang Lebih Halus dari Saringan 75 μm (No. 200) dalam Agregat Mineral dengan Pencucian. Jakarta: Badan Standardisasi Nasional.

SNI ASTM C136:2012. 2012. Metode Uji Untuk Analisis Saringan Agregat Halus dan Agregat Kasar. Jakarta: Badan Standarisasi Nasional.

Spesifikasi Umum Bina Marga. 2018. Divisi 6 Perkerasan Aspal. Surabaya: DPU Bina Marga.

Published
2021-08-02
How to Cite
Habibah, I. M., Rifqi, M. G., & Pranowo, D. D. (2021). Pengaruh Pemanfaatan Plastik Polyethylene Terephalate Pada Campuran Laston Lapis Pengikat. Journal of Applied Civil Engineering and Infrastructure Technology, 2(1), 6-11. https://doi.org/10.52158/jaceit.v2i1.70
Section
Articles